TOPIC: Nano-Cloth Studies - Series 1

Re: Nano-Cloth Studies - Series 1 9 months ago #4787

  • AnthonyYan
  • OFFLINE
  • Senior Boarder
  • Posts: 67
  • Karma: 10
wickededge wrote:
I started by preparing a bunch of samples with super polished bevels so we would be able to clearly see the effects of various abrasives.


Hi Clay,

Fascinating pictures! I'm curious, how did you "super polish" the edge to begin with?

Sincerely,
--Lagrangian
Reply Quote

Re: Nano-Cloth Studies - Series 1 8 months, 2 weeks ago #5225

  • BassLakeDan
  • OFFLINE
  • Expert Boarder
  • Posts: 116
  • Karma: 19
wickededge wrote:
.. super polished bevels..
25um-Clean-Strop-1.jpg

..


Clay,

I have been meaning to ask, 1.) what steel is this that you were using for these tests, and 2.) what RC? Just curious ... thanks
Reply Quote

Re: Nano-Cloth Studies - Series 1 8 months, 2 weeks ago #5230

  • wickededge
  • OFFLINE
  • Administrator
  • Posts: 1411
  • Karma: 75
AnthonyYan wrote:
wickededge wrote:
I started by preparing a bunch of samples with super polished bevels so we would be able to clearly see the effects of various abrasives.


Hi Clay,

Fascinating pictures! I'm curious, how did you "super polish" the edge to begin with?

Sincerely,
--Lagrangian


I progressed through the usual diamond plates, then on to the Micro-Fine ceramics and then used 1um diamond on cow leather, .5um diamond on cow leather, .25um diamond on kangaroo and then .125 CBN on kangaroo. I didn't spend so much time as to remove every last scratch, just the vast majority.
--Clay Allison
Reply Quote
The following user(s) said Thank You: AnthonyYan

Re: Nano-Cloth Studies - Series 1 8 months, 2 weeks ago #5231

  • wickededge
  • OFFLINE
  • Administrator
  • Posts: 1411
  • Karma: 75
BassLakeDan wrote:
wickededge wrote:
.. super polished bevels..
..


Clay,

I have been meaning to ask, 1.) what steel is this that you were using for these tests, and 2.) what RC? Just curious ... thanks


I've been using a bunch of utility blades from the same 100 pc pack so that they are very similar. They're listed as "high carbon" though I don't know exactly what the composition or hardness is. If I had to guess, I'd put the hardness around 57-58 HRC.
--Clay Allison
Reply Quote

Re: Nano-Cloth Studies - Series 1 8 months, 2 weeks ago #5246

wickededge wrote:
AnthonyYan wrote:
wickededge wrote:
I started by preparing a bunch of samples with super polished bevels so we would be able to clearly see the effects of various abrasives.


Hi Clay,

Fascinating pictures! I'm curious, how did you "super polish" the edge to begin with?

Sincerely,
--Lagrangian


I progressed through the usual diamond plates, then on to the Micro-Fine ceramics and then used 1um diamond on cow leather, .5um diamond on cow leather, .25um diamond on kangaroo and then .125 CBN on kangaroo. I didn't spend so much time as to remove every last scratch, just the vast majority.


So you did ship the Super fine 1200/1600 in this case? Did it take you much longer with the next ceramics since you did skip the fist?
Reply Quote

Re: Nano-Cloth Studies - Series 1 8 months, 2 weeks ago #5247

  • wickededge
  • OFFLINE
  • Administrator
  • Posts: 1411
  • Karma: 75
SvenSchläfke wrote:

So you did ship the Super fine 1200/1600 in this case? Did it take you much longer with the next ceramics since you did skip the fist?


In this case I did skip them and it took a little longer, but not too bad, partly because my diamond plates are so well worn in now that they're already doing a lot of polishing before I even get to the ceramics.
--Clay Allison
Reply Quote